ASTM B 211

1.1 This specification covers rolled or cold-finished bar, rod, and wire in alloys (Note 1) and tempers as shown in Table 2. Note 1 -Throughout this specification use of the term alloy in the general sense includes aluminum as well as aluminum alloy. Note 2 -The term cold finished is used to indicate the type of surface finish, sharpness of angles, and dimensional tolerances produced by drawing through a die. Note 3 -See Specification B221 for aluminum and aluminum-alloy extruded bars, rods, wire, shapes, and tubes; and Specification B316/B316M for aluminum and aluminum-alloy rivet and cold-heading wire and rods. 1.2 Alloy and temper designations are in accordance with ANSI H35.1. The equivalent UNS alloy designations are those of Table 1 preceded by A9, for example, A91100 for aluminum 1100 in accordance with Practice E527 . 1.3 A complete metric companion to Specification B211 has been developed B211M; therefore, no metric equivalents are presented in this specification. 1.4 For acceptance criteria for inclusion of new aluminum and aluminum alloys in this specification, see Annex A2. TABLE 1 Chemical Composition Limits A <(hoch),> B <(hoch),> C <(hoch),> D Alloy Si Fe Cu Mn Mg Cr Ni Zn Ti Bi Pb Sn Other Elements E Aluminum Each Total F 1100 0.95 Si + Fe 0.05 - 0.20 0.05 ... ... ... 0.10 ... ... ... ... 0.05 0.15 99.00 min G 2011 0.40 0.7 5.0 - 6.0 ... ... ... ... 0.30 ... 0.20 - 0.6 0.20 - 0.6 ... 0.05 0.15 remainder 2014 0.50 - 1.2 0.7 3.9 - 5.0 0.40 - 1.2 0.20 - 0.8 0.10 ... 0.25 ... ... ... 0.15 0.05 0.15 remainder 2017 0.20 - 0.8 0.7 3.5 - 4.5 0.40 - 1.0 0.40 - 0.8 0.10 ... 0.25 ... ... ... 0.15 0.05 0.15 remainder 2024 0.50 0.50 3.8 - 4.9 0.30 - 0.9 1.2 - 1.8 0.10 ... 0.25 ... ... ... 0.15 0.05 0.15 remainder 2219 0.20 0.30 5.8 - 6.8 0.20 - 0.40 0.02 ... ... 0.10 ... ... ... 0.02 - 0.10 0.05 H 0.15 H remainder 3003 0.6 0.7 0.05 - 0.20 1.0 - 1.5 ... ... ... 0.10 ... ... ... ... 0.05 0.15 remainder 4032 11.0 - 1 ....(abbreviated)